Specification |
Supply Form |
Others |
Sheet |
Thickness:0.40-4.75mm,General Width:1000,1219,1500mm |
Whole Coil or piece of it |
Cold Annealed,Surface 2B,2E |
Plate |
Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,8000,8500mm(Under 10mm plate can be coiled) |
Whole Coil or piece of it |
Single hot rolling,Solid solution annealed state,Surface 1D |
Belt |
Thickness:0.10-3.0mm,Width:50-500mm |
Whole Coil or Specified size |
Cold Annealed,Surface 2B,2E |
Bar & Rod |
Rolled barΦ5-45mm,Length≤1500mm |
Polished Bar(circle,Square) |
Solution annealing,descaling |
Forged barΦ26-245mm,Length≤4000mm |
Element |
Content (%) |
|---|---|
| Nickel, Ni | 58-63 |
| Chromium, Cr | 21-25 |
| Aluminum, Al | 1-1.7 |
| Copper, Cu | 1 |
| Manganese, Mn | 1 |
| Silicon, Si | 0.5 |
| Carbon, C | 0.1 |
| Sulfur, S | 0.015 |
| Iron, Fe | Balance |
Properties |
Metric | Imperial |
|---|---|---|
| Density | 8.11 g/cm3 | 0.293 lb/in3 |
| Melting point | 1360-1411°C | 2480-2572°F |
Properties |
Metric | Imperial |
|---|---|---|
| Tensile strength (Solution annealed) | 760 MPa | 110000 psi |
| Yield strength (Solution annealed) | 450 MPa | 65300 psi |
| Elongation at break (Solution annealed) | 42% | 42% |
Properties |
Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 13.75 µm/m°C | 7.639 µin/in°F |
| Thermal conductivity | 11.2 W/mK | 77.7 BTU.in/hrft².°F |