| Application: | Industrial |
|---|---|
| Standard: | GB, ASTM |
| Purity: | >99.99% |
| Alloy: | Alloy |
| Powder: | Not Powder |
| Size: | 3/8 to 2 Inch |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Form |
Specification |
Supply Form |
Others |
Sheet |
Thickness:0.40-4.75mm,General Width:1000,1219,1500mm |
Whole Coil or piece of it |
Cold Annealed,Surface 2B,2E |
Plate |
Thickness:4.76-60mm,Width:1500,2000,2500mm,Length:3000,6000,8000,8500mm(Under 10mm plate can be coiled) |
Whole Coil or piece of it |
Single hot rolling,Solid solution annealed state,Surface 1D |
Belt |
Thickness:0.10-3.0mm,Width:50-500mm |
Whole Coil or Specified size |
Cold Annealed,Surface 2B,2E |
Bar & Rod |
Rolled barΦ5-45mm,Length≤1500mm |
Polished Bar(circle,Square) |
Solution annealing,descaling |
Forged barΦ26-245mm,Length≤4000mm |
Element |
Content |
Nickel (Ni) |
72 % min |
Chromium (Cr) |
14 - 16 % |
Iron (Fe) |
6 - 10 % |
Property |
Metric |
Imperial |
Density |
8.47 g/cm3 |
0.306 lb/in3 |
Melting point |
1413 °C |
2575°F |
Co-Efficient of Expansion |
13.3 µm/m.°C (20-100°C) |
7.4x10-6 in/in.°F (70-212 °F) |
Modulus of rigidity |
75.6 kN/mm2 |
10965 ksi |
Modulus of elasticity |
206 kN/mm2 |
29878 ksi |
Condition of Supply |
Heat Treatment (After Forming) |
|||
Annealed/Spring Temper |
Stress relive at 460°C (860°F) for 1hr and air cool. |
|||
Condition |
Approx Tensile Strength |
Approx Service Temp. |
||
Annealed |
600-750 N/mm2 |
87-109 ksi |
-200 to +330°C |
-330 to +625°F |
Spring Temper |
900-1250 N/mm2 |
131-181 ksi |
-200 to +330°C |
-330 to +625°F |