Audited Supplier Corrosion resistant alloy Inconel 601
Inconel 601, an alloy material. Excellent oxidation resistance at high temperature, good carbonization resistance, good oxidation resistance in sulfur-containing atmosphere, good mechanical properties at both room temperature and high temperature Good stress corrosion cracking resistance due to controlled Carbon content and grain size, 601 has higher creep rupture strength, so it is recommended to use 601 in the field above 500 ºC.
Chemical composition
Alloy grade % nickel chromium iron carbon manganese silicon copper aluminum phosphorus sulfur
601 minimum 58 21 1.0
maximum 63 25 margin 0.1 1.5 0.5 1 1.7 0.02 0.015
Physical properties
Density 8.1 g/cm3
melting point 1320-1370ºC
Minimum mechanical properties of the alloy at room temperature:
Alloy and Condition Tensile strength Rm N/mm2 Yield strength RP0.2N/mm2 Elongation A5 % Brinell hardness HB
Annealing 650 300 30 -
Solution treatment 600 240 30 ≤220
Chemical characteristics
1. Excellent oxidation resistance at high temperature
2. Good carbonization resistance
3. Good oxidation resistance in sulfur-containing atmosphere
4. Good mechanical properties at both room temperature and high temperature
5. Good resistance to stress corrosion cracking. Due to the control of carbon content and grain size, 601 has high creep rupture strength, so 601 is recommended in the field above 500 °C.
Metallographic structure of Inconel 601:
601 is a face-centered cubic lattice structure.
Corrosion resistance of Inconel 601:
An important property of alloy 601 is its resistance to oxidation at temperatures up to 1180°C. Even under severe conditions, such as during heating and cooling cycles, 601 produces a dense oxide film for high spalling resistance. 601 has very good carbonization resistance. Due to its high chromium and aluminum content, 601 has good oxidation resistance in high temperature sulfur-containing atmospheres.
Application
1. Trays, baskets and fixtures for heat treatment factories.
2. Steel wire split annealing and radiant tubes, high-speed gas burners, wire mesh belts in industrial furnaces.
3. Isolation tanks in ammonia reforming and catalytic support grids in nitric acid production.
4. Exhaust system components
5. Combustion chamber of solid waste incinerator
6. Duct Support and Soot Handling Components
7. Exhaust gas detoxification system components
8. Oxygen reheater