The gh2132 alloy is a Fe-25Ni-15Cr-based superalloy, which is comprehensively strengthened by adding molybdenum, titanium, aluminum, vanadium and a trace amount of boron.
It has high yield strength and lasting and creep strength below 650ºC, and has good processing plasticity and satisfactory welding performance.
It is suitable for the manufacture of high-temperature load-bearing components of aero-engines that work for a long time below 650 °C, such as turbine disks, compressor disks, rotor blades and fasteners.
The alloy can produce various shape deformed products, such as: discs, forgings, plates, rods, wires and rings.
Similar material grade: ZbNCT25 (France)
Material Specifications: Specification for Cold Drawn Bars of Superalloys for Aeronautics
Chemical composition
The chemical composition of the alloy is shown in Table 1-1
C Cr Ni Mo Ti Fe
≤0.08 13.5~16.0 24.0~27.0 1.00~1.50 1.90~2.30 Remain
V B Mn Al Si P S
0.10~0.50 0.001~0.010 1.00~2.00 ≤0.35 ≤1.00 ≤0.030 ≤0.020
Note: 1 The standard for cold drawn rods, round cakes and ring blanks stipulates (Ti) 1.80%~2.35%.
2 Hot-rolled and cold-rolled sheet standards stipulate (B) 0.003%~0.010%, (Mn)≤2.00%, (P)≤0.020%, (S)≤0.015%.
3 The cold drawing wire standard stipulates (Al)≤0.35%, (Ti)1.75%~2.35%, (Si)0.40%~1.00%, (P)≤0.020%, (S)≤0.015%.
4 Standard regulations for wire for cold heading (Ti) 1.75%~2.35%, (Si) 0.40%~1.00%, (P)≤0.025%, (S)≤0.020%.
5 Standard requirements for hot rolled and forged bars (Cu) ≤ 0.25%.
1.5.) Heat treatment system The heat treatment system specified by the material standard is shown in Table 1-3; the heat treatment system for high-quality alloys is 900ºC±10ºC, 1-2h, oil cooling +750ºC±10ºC, 16h, air cooling.
Table 1-3
Material variety
Heat treatment system
Bars, round cakes
980~1000ºC, 1~2h, oil cooling +700~720ºC, 12~16h, air cooling
Hot rolled sheet, cold rolled sheet
980~1000ºC, air cooling +700~720ºC, 16h, air cooling
cold drawn rod
980~1000ºC, 1~2h, oil cooling +700~720ºC, 16h, air cooling
Ring blank
980~990ºC, 1~2h, oil cooling +700~720ºC, 15h, air cooling
Cold drawing for cold heading
980~1000ºC, 1~2h, water cooling or oil cooling +700~720ºC, 16h, air cooling
Note: The standard for cold drawn rods and cold heading wires stipulates that when the performance test fails, the aging time at 760°C can be no more than 16h, and the delivery is made after passing the test.
Physical and chemical properties
Thermal performance
Melting temperature range 1364~1424ºC
Density ρ=7.93g/cm3