K465 is a nickel-based alloy, which belongs to the precipitation hardening equiaxed crystal casting superalloy. The alloy elements are relatively complex, and it needs to be smelted in a vacuum induction furnace. The smelted mother alloy is poured into various precision parts and bars and plates. On the basis of nickel, elements such as chromium, cobalt, tungsten and aluminum are added to make the alloy have good high temperature resistance (recommended to be used in an environment below 1050 degrees Celsius), and at the same time have good strength and corrosion resistance, good comprehensive performance, and the range of use is also It is widely used, such as blades and guides used in turbines, and has good casting performance. After long-term samples, it can be made into various complex parts.
Chemical composition of K465:
Element C Cr Ni Co W Mo
Mass fraction/% 0.13~0.20 8~9.50 Balance 9.00~10.50 9.5~11.00 1.20~2.40
Elements Al Ti Nb B Zr Fe
Mass fraction/% 5.10~6.00 2.00~2.90 0.8~1.2 ≤0.035 ≤0.04 ≤1
Elements Ce Y Si P S Mn Pb Bi
Mass fraction/% ≤0.02 ≤0.01 ≤0.4 ≤0.015 ≤0.01 ≤0.4 ≤0.001 ≤0.0005
Species
The mother alloy is cast into a round long rod, the diameter of which ranges from 75mm to 90mm, and the length is not less than 250mm.
supply status
Master alloys are supplied as-cast, and precision castings are supplied as-cast or after heat treatment.
Physical, elastic and chemical properties
Melting temperature range
Initial melting point: 1250 ° C (metallographic method), 1300 ° C ~ 1338 ° C (differential thermal analysis method) 2].
Density: p=8.341g/cmCll.
Magnetic properties: The alloy is non-magnetic.